| Specification | ProcessDescription | Category | SpecLimits |
| 2ZZP00001 | Finish Specification for F-35 Weapon System. Note* Approval for this specification is required in conjunction with MIL-PRF-8625 for appropriate anodize seal requirements | Limits: This spec shall be used in conjunction with MIL-PRF-8625 for appropriate anodize and sealing type | |
| AMS 2700 | Passivation Treatments for Corrosion-Resistant Steel | Chemical Processing | Limits: Method 1 Type 2 & 6 only |
| AMS-QQ-P-416 | Plating, Cadmium (Electrodeposited). | Chemical Processing | Limits: None |
| ASTM B117 | Standard Practice for Operating Salt Spray (Fog) Apparatus | Non-Destructive Testing | Limits: Internal Processing Only |
| ASTM E1417 | Standard Practice for Liquid Penetrant Testing | Non-Destructive Testing | Limits: None |
| ASTM E1444 | Standard Practice for Magnetic Particle Testing | Non-Destructive Testing | Limits: None |
| ASTM E18 | Standard Test Methods for Rockwell Hardness of Metallic Materials. Required for F35 program only | Materials Testing | Limits: None |
| LMA-PC009 | Hardness and Conductivity Testing | Miscellaneous | Limits: None |
| LMA-PC201 | Fluorescent Penetrant Inspection of Metallic Parts & Materials | Non-Destructive Testing | Limits: Limited to normal control, non critical parts. |
| LMA-PG001 | Etch/Cleaning Prior to Penetrant Inspection | Chemical Processing | Limits: Limited to etching Aluminum and Titanium parts only |
| LMA-PJ013 | Touch-up Requirements for Chemical and Organic Finishes | Chemical Processing | Limits: None |
| LMA-PJ264 | Application and Control of Organic Finishes | Chemical Processing | Limits: None |
| MIL-DTL-5541 | Chemical Conversion Coatings for Aluminum and Aluminum Alloy | Chemical Processing | Limits: None |
| MIL-PRF-46010 | Dry Film Lube Superseded by AS5272 for Ty I & II only | Chemical Processing | Limits: None |
| MIL-PRF-8625 | Anodic Coatings For Aluminum and Aluminum Alloys | Chemical Processing | Limits: Dichromate seal is required when Mil-PRF-8625 anodize is called out on engineering drawings |